RAPID PROTOTYPING | Vaccum Casting Polyurethanes Resins
| References | Description | Color | Flexural modulus (MPa) | Hardness shore | Tg (°C) | Applications |
|---|---|---|---|---|---|---|
|
PX 223 HT |
Low viscosity. Impact resistant. High heat resistance. |
Black |
2300 |
80D |
>120 |
Prototype parts ABS like. |
|
PX 226 SYSTEM |
Long pot life |
white |
2,500 |
82 |
105 |
Used by vacuum casting in silicon moulds for making prototype parts and mock-ups with mechanical properties similar to thermoplastics like polystyrene and filled ABS. |
|
PX 234 HT / 234 HT LS |
High temperature resistance. Easy casting. |
Light amber |
1850 |
80D |
220 |
Similar to PPS, PEEK. All parts needed high temperature resistance . |
|
PX 245 SYSTEM |
High flexural modulus of elasticity |
off-white |
4,500 |
80-85 |
95 |
To be used by vacuum casting in silicone moulds for making prototype parts and mock-ups with mechanical properties similar to thermoplastics like polyoxymethylene and polyamide. |
|
PX 330 |
FAR 25 certification (fire resistance). Easy to process. |
Off-white |
3400 |
87 D |
100 |
Technical parts for aeronautics. All parts where fire certification is needed. |
|
PX 5210 / 5211 |
High transparency Good U.V. resistance |
transparent |
2,000 |
85 |
90 |
transparent prototype parts until a 50 mm thickness crystal glass parts art/decoration parts |
|
PX 5210 / 5212 |
High transparency Good U.V. resistance |
transparent |
2,400 |
85 |
95 |
transparent prototype parts until a 10 mm thickness crystal glass parts fashion, jewellery, art and decoration parts, lenses for lights |
|
PX 527 |
Clear vacuum casting polyurethane resin. Fast demoulding, good impact and flexural resistance. Clear aspect. |
transparent |
2600 |
80 |
90 |
To be used by vacuum casting in silicon moulds for making prototypes parts and mock-ups with mechanical properties similar to thermoplastics like ABS types or PC. |
| References | Description | Color | Flexural modulus (MPa) | Hardness shore | Tg (°C) | Applications |
|---|---|---|---|---|---|---|
|
PX 100 |
Low viscosity. Can be applied by hand. |
Off-white |
1500 |
74D |
75 |
Prototype parts like H.I.PS. |
|
PX 2017 HT - 223 HT |
Low viscosity for easy casting, good impact and flexural resistance, temperature resistance above 120 °C and low aggressiveness against silicon moulds |
Black |
1.600 |
80 - 70 Shore D |
- |
Used by casting in silicone moulds for the realisation of prototype parts and mock-ups whose mechanical properties are close to those of thermoplastics |
|
PX 205 |
"""Unbreakable, hinge effect""." |
Cream to dark beige |
500 |
70D |
100 |
Similar to PEHD or PP. |
|
PX 212 |
Low viscosity. Faster moulding time. Impact resistance. |
Translucent |
1200 |
76D |
90 |
Prototype parts PP with good temperature resistance. |
|
PX 215 |
Processing under vacuum recommended. High reproduction accuracy. This product can be easily pigmented with colouring CP. Low aggressive against silicone toolings. |
Off-white |
1.500 |
74 65 |
75 |
Used by casting in silicone moulds for the realisaton of prototype parts and mock-ups whose mechanical properties are close to those of thermoplastics. |
|
PX 217 |
Short demoulding time. High impact resistance. |
Cream beige |
1700 |
77D |
100 |
Similar to High impact PS. |
| References | Description | Color | Flexural modulus (MPa) | Hardness shore | Tg (°C) | Applications |
|---|---|---|---|---|---|---|
|
PX 761 |
High heat resistance. Long pot life. |
Amber |
_ |
63A |
_ |
Rubber like prototype parts. |
|
PX 774 |
Low viscosity. Very short demoulding time. |
Black |
_ |
75A |
_ |
Rubber like prototype parts. |
|
UPX 8400 |
3 components for variable hardness Fixed mix ratio Easy to pigment with CP color system Low silicone moulds agressivity
|
Off white
|
N/A
|
95A1
|
N/A
|
Using by casting under vacuum in silicone moulds to make soft prototype parts or small series of rubber like parts.
|